Crystal Structures and Piezoelectric Properties of Quenched and Slowly-Cooled BiFeO₃-BaTiO₃ Ceramics

The BiFeO₃-BaTiO₃ (BF-BT) ceramics were here prepared through the solid-state reaction of Bi₂O₃, Fe₂O₃ and nano-sized BT powders. The crystal structures and piezoelectric properties were investigated in both quenched (AQ) and slowly cooled (SC) 0.7BF-0.3BT ceramics. Prior work has shown that rhombohedral and pseudo-cubic phases coexist in 0.7BF-0.3BT ceramics. In this work, the crystal structure of the pseudo-cubic phase was refined as a non-polar orthorhombic Pbnm phase in the SC sample and as a polar orthorhombic Pmc2₁ phase in the AQ sample. In addition to a sharp dielectric peak at about 620 °C, corresponding to the Curie temperature of the rhombohedral phase, a broad dielectric peak with strong frequency dispersion and a sharp frequency-independent dielectric peak were observed at around 500 °C in the SC and AQ samples, respectively. We determine that the dielectric anomalies around 500 °C were caused by a relaxor phase transition of the non-polar orthorhombic phase in the SC sample and a ferroelectric-paraelectric phase transition of the polar orthorhombic phase in the AQ sample. The AQ sample showed better ferroelectric and piezoelectric properties than the SC sample. The 0.7BF-0.3BT ceramic slowly cooled in a nitrogen atmosphere showed a well-saturated P-E curve and a similar temperature-dependent dielectric constant as the AQ sample. Our results indicate that large concentrations of oxygen vacancies produce a more distorted polar orthorhombic phase and better piezoelectric properties in the AQ sample than in the SC sample.