Surface Topography Analysis of BK7 with Different Roughness Nozzles Using an Abrasive Water Jet

This study investigated the effect of abrasive water jet (AWJ) kinematic parameters, such as jet traverse speed and water pressure, abrasive mass flow rate, and standoff distance on the surface of BK7. Nozzle A reinforced with a 100 nm particle-sized coating of titanium alloy has more wear resistance compared to Nozzle B coated with nothing. Through analysis of variance and measurement of BK7 surface quality, it is concluded that the grooving and plowing caused by abrasive particles and irregularities in the abrasive water jet machined surface with respect to traverse speed (3, 7.2, 7.8, and 9 mm/min), abrasive flow rate (7 L/min and 10 L/min, 80 mesh) and water pressure (2 and 3 MPa) were investigated using surface topography measurements. The surface roughness (15.734 nm) of BK7 results show that a nozzle coated with titanium alloy has more hardness, which protects BK7 undamaged and super-smooth. The values of selected surface roughness profile parameters-average roughness (Ra) and maximum height of PV (maximum depth of peak and valleys)-reveal a comparatively smooth BK7 surface in composites reinforced with 2% titanium alloy in the nozzle weight at a traverse speed of 7.8 mm/min. Moreover, abrasive water jet machining at high water pressure (3 MPa) produced better surface quality due to material removal and effective cleaning of lens fragmentation and abrasive particles from the polishing zone compared to a lower water pressure (2 MPa), low traverse speed (5 mm/min), and low abrasive mass flow rate (200 g/min).