The Synergistic Effect of Calcained Coal-Series Kaolinite and Limestone on the Hydration of Portland Cement

Limestone calcined clay cement (LC³) presents a promising alternative material due to its reduced CO₂ emissions and superior mechanical properties compared to traditional Portland cement (PC). This study investigates the synergistic effect of calcined coal-series kaolinite (CCK) and limestone (LS) on the hydration behavior of cement, specifically focusing on varying mass ratios. The combination of CCK and LS promotes the formation of strätlingite and carboaluminates, which enhances early-age strength development. Additionally, the inclusion of CCK facilitates the formation of carboaluminates during later stages of hydration. After 56 days of hydration, the content of carboaluminates is over 10%wt. This stimulation of secondary hydration products significantly refines the evolution of pore structure, with the harmful large pores gradually transformed into harmless medium pores and gel pores, leading to marked improvements in compressive strength from 7 to 28 days. Replacing 45% PC with CCK and LS at mass ratio of 7 to 2, the compressive strength of blends reaches 47.2 MPa at 28 days. Overall, the synergistic interaction between CCK and LS presents unique opportunities to minimize the CO₂ footprint of the cement industry without compromising early and long-term performance.