Evaluation of Mechanical Properties of Composite Material with a Thermoplastic Matrix Reinforced with Cellulose...

Low-density polyethylene (LDPE) has been widely used in various applications due to its flexibility, lightness, and low production cost. However, its massive use in disposable products has raised environmental concerns, prompting the search for more sustainable alternatives. This study aims to investigate the mechanical properties achievable in a composite material utilizing low-density polyethylene (LDPE), potato starch (PS), and cellulose microfibrils (MFCA) at loadings of 0.05%, 0.15%, and 0.30%. Initially, the cellulose acetate microfibrils (MFCA) were produced via an electrospinning process. Subsequently, a dispersive mixture of the aforementioned materials was created through the extrusion and pelletizing process to form pellets. These pellets were then molded by injection molding to produce test specimens in accordance with ASTM D 638, the standard for tensile strength testing. The evaluation of the properties was conducted through mechanical tensile tests (ASTM D638), hardness tests (ASTM D 2240), melt flow index (ASTM D1238), and scanning electron microscopy (SEM). This study determined the influence of cellulose acetate microfibril loadings below 0.3% as reinforcement within a thermoplastic LDPE matrix. It was demonstrated that these microfibrils, due to their length-to-diameter ratio, contribute to an enhancement in the mechanical properties.