Topological Synthesis of 2D High-Entropy Multimetallic (Oxy)hydroxide for Enhanced Lattice Oxygen Oxidation Mechanism

Owing to sluggish reaction kinetics and high potential, oxygen evolution reaction (OER) electrocatalysts face a trade-off between activity and stability. Herein, an innovative topological strategy is presented for preparing 2D multimetallic (oxy)hydroxide, including ternary CoFeZn, quaternary CoFeMnZn, and high-entropy CoFeMnCuZn. The key to the synthesis lies in using Ca-rich brownmillerite oxide as a precursor, which possesses inherent structural flexibility enabling tailored elemental adjustments and topologically transforms from a point-shared structure of metal-oxygen octahedrons into an edge-shared structure under alkaline conditions. The presence of Zn in the catalysts causes a shift in the center of the O2p band toward the Fermi level, resulting in more Co⁴⁺ species, which drive holes into oxygen ligands to promote intramolecular oxygen coupling. The triggered lattice oxidation mechanism is identified by detecting peroxo-like (O₂ ^2-) negative species using tetramethylammonium chemical probe, along with ¹⁸O isotope labeling experiments. As a result, the catalyst demonstrates an overpotential of 267 mV at 10 mA cm^-2, ranking it among the top-performing non-Ni-based catalysts. Importantly, the catalysts also show high Fe-leaching resistance during OER compared to conventional NiFe and CoFe hydroxides/(oxy)hydroxides. The assembled zinc-air battery enables stable operation for over 225 h at a low charging voltage of 1.93 V.