The effects of environments and adhesive layer thickness on the failure modes of composite material bonded joints

In this study, a structural adhesive was used to bond unidirectional prepreg and fiber fabric in a single lap joint. The mechanical properties of the structural adhesive were investigated under room temperature dry state (RTD) and elevated temperature wet state (ETW, 71 ℃/85% RH), and different adhesive layer thicknesses (0.5 mm, 1.0 mm, 1.5 mm, and 2.0 mm). The fracture surfaces of the bonded joints were examined using scanning electron microscopy (SEM), and finite element simulations were conducted to observe the failure modes and failure paths. Additionally, the specimens were immersed in water and hydraulic oil, and their tensile shear strength was tested to evaluate their liquid sensitivity. The experimental results indicated that with increasing adhesive layer thickness, the strength of the specimens decreased by 21% in the RTD and by 52% in the ETW. The strength differences between different environments were minimal for adhesive layer thicknesses of 1 mm and 1.5 mm. The shear strength of the specimens decreased after immersion in water and hydraulic oil, with reductions of 43.78% and 39.21%, compared to the room temperature dry respectively. SEM observations of the bonded joint sections revealed that the primary failure modes were adherend failure and adhesive layer failure. Finite element simulations indicated that fiber tearing and crack initiation occurred in stress concentration areas during loading, leading to structural failure.