Comparative Evaluation of the Mechanical Efficiency of Nanosilver Fluoride and Sodium Fluoride Varnish: An In Vitro Study
Related Experiment Video
Updated: Jun 11, 2025
Evaluation of Antimicrobial Activities of Nanoparticles and Nanostructured Surfaces In Vitro
Published on: April 21, 2023
Sahana Kritivasan1, Hp S Sogi1, Mansi Jain1
1Department of Pediatric and Preventive Dentistry, Maharishi Markandeshwar College of Dental Sciences and Research, Maharishi Markandeshwar (Deemed to be University), Ambala, Haryana, India.
Background:
Dental caries is the most common disease in childhood and has an impact on general health status. The topical application of fluoride varnishes has been used for the prevention and control of dental caries due to their high fluoride content, adhesion capacity, and safety. Silver has a varied application in medicine as well as in dentistry due to its anticaries, antimicrobial, and antirheumatic potentials. The introduction of nanosilver fluoride (NSF) was made with advancements in technology to overcome the drawbacks of silver diamine fluoride (SDF).
Aim:
To compare and evaluate the microhardness and microleakage of NSF varnish and sodium fluoride (NaF) varnish.
Materials And Methods:
An in vitro comparative experimental study was carried out between synthesized NSF and commercially available NaF, with 20 samples in each group. The specimens were sectioned and subjected to microhardness evaluation using Vickers microhardness testing and the dye penetration method to evaluate the microleakage.
Results:
The average microhardness was found to be 230.7218 VMH for NSF (group I), 198.9841 VMH for NaF (group II), and 91.6120 VMH for group III. These differences were statistically significant when compared with each other (p = 0.002). In 50% of the samples, no dye penetration was seen in the NSF group, compared to the NaF varnish group, where 75% of the samples exhibited penetration onto the varnish interface or the varnish and tooth interface.
Conclusion:
Nanosilver fluoride proves to be an effective alternative to commercially available topical fluoride agents such as NaF. It has greater microhardness and lower microleakage than NaF and the control teeth.
Clinical Significance:
Nanosilver fluoride varnish can be used as a cost-effective alternative to NaF varnish and SDF. It can be applied with minimal training by healthcare workers or general practitioners.
How To Cite This Article:
Kritivasan S, Sogi HS, Jain M, et al. Comparative Evaluation of the Mechanical Efficiency of Nanosilver Fluoride and Sodium Fluoride Varnish: An In Vitro Study. Int J Clin Pediatr Dent 2024;17(5):539-544.
More Related Videos
08:20Systematic Approach to Identify Novel Antimicrobial and Antibiofilm Molecules from Plants' Extracts and Fractions to Prevent Dental Caries
Published on: March 31, 2021
09:31Fluorescence-based Neuraminidase Inhibition Assay to Assess the Susceptibility of Influenza Viruses to The Neuraminidase Inhibitor Class of Antivirals
Published on: April 15, 2017