Preparation and characterization of mesoporous HA coating with paclitaxel loaded lignin nanospheres on titanium
Baoe Li1, Xiaopeng Fu1, Donghui Wang1
1School of Materials Science and Engineering, Hebei University of Technology, Tianjin, 300130, China.
Background:
Primary malignant bone tumor is a disease that can lead to death. The usually applied clinical treatment strategy is surgical resection of the primary tumor. However, tumor cells are difficult to clean up, easy to make the tumor recurrence, and the bone defect caused by surgical resection also hindered the postoperative recovery.
Materials And Methods:
Herein, in this work, mesoporous hydroxyapatite (HA) coating with petal-structure was prepared on titanium (Ti) implant surfaces by micro-arc oxidation (MAO) to accelerate the bone growth, and then paclitaxel (PTX) loaded lignin nanospheres were deposited into the HA coatings to get a sustained release for killing residual tumor cells.
Results:
The results showed that many gaps and holes of micro-scale were formed in the petal-structured HA coatings, they worked as traps for the PTX loaded nanospheres to enhance the deposited amount and immobilization stability, playing good role of drug loading platform. The encapsulation of PTX by lignin ensured a lower release rate and a higher sustaining release time when compared with the PTX without encapsulation. In addition, the HA coating with PTX loaded lignin nanospheres showed higher killing effect to tumor cells than to osteoblast.
Conclusion:
The mesoporous HA coating with paclitaxel loaded lignin nanospheres endowed the titanium surface with good biological property and tumor cell-killing effect, so the obtained Ti-based material had a highly hopeful application as the localized implant for therapy of primary malignant bone tumor.