Linear polydichlorophosphazene and Ti₃C₂T_x MXene nanohybrids: Synthesis and application to epoxy resin to improve the...

Enhancing the fire safety of epoxy resins (EPs) typically requires a significant amount of flame retardants, which often results in considerable degradation of their mechanical properties. To address this issue, a novel flame retardant known as PDCP@DPA@MXene was synthesized and integrated into EP to achieve notable improvements in flame retardancy, smoke suppression, and mechanical strength. By incorporating 1.5 wt% PDCP@DPA@MXene, the impact strength, tensile strength, and elongation at break of the resulting PDM-1.5 %/EP composite reached 12.1 kJ/m², 57.4 MPa, and 13.0, respectively, reflecting enhancements of 63.5 %, 18.4 %, and 17.1 % compared to the pure EP. The enhancement in tensile strength may be attributed to the high rigidity of Ti₃C₂T_x MXene, which reinforces the EP matrix. Additionally, the intertwined structure of PDCP@DPA@MXene chains effectively mitigates material fracturing and absorbs impact forces, thus toughening the EP. The presence of phosphorus, nitrogen, and titanate in PDCP@DPA@MXene contributes to the formation of a more compact char layer. The PDM-1.5 %/EP sample achieved a V-0 rating in the vertical UL-94 test and exhibited a high limiting oxygen index of 32.0. Furthermore, the sample containing 2 wt% PDCP@DPA@MXene showed a significant reduction in peak heat release rate (p-HRR) and total heat release (THR), recording values of 689 kW/m² and 71.9 MJ/m², which are decreases of 45.1 % and 26.9 %, respectively, compared to pure EP. Additionally, the incorporation of PDCP@DPA@MXene led to a reduction in CO production. These flame-retarded EPs demonstrate strong potential for various applications due to their elevated glass transition temperature and robust thermal stability.