A(CoFe)(S2)2/CoFe heterostructure constructed in S, N co-doped carbon nanotubes as an efficient oxygen
Bowen Yuan1, Bin Liu1, Jin Liu1
1Heilongjiang Provincial Key Laboratory of Environmental Nanotechnology and Key Laboratory of Functional Inorganic Material Chemistry, Ministry of Education of the People's Republic of China, School of Chemistry and Materials Science, Heilongjiang University, Harbin 150080, China.
Abstract:
Transition metal alloys can exhibit synergistic intermetallic effects to obtain high activities for oxygen reduction/evolution reactions (ORR/OER). However, due to the insufficient stability of active sites in alkaline electrolytes, conventional alloy catalysts still do not meet practical needs. Herein, by using polypyrrole tubes and cobalt-iron (CoFe) Prussian blue analogs as precursors, CoFe sulfides is in-situ formed on CoFe alloys to construct (CoFe)(S2)2/CoFe heterostructure in sulfur (S) and nitrogen (N) co-doped carbon nanotubes (CoFe@NCNTs-nS) via a low-temperature sulfidation strategy. The as-marked CoFe@NCNTs-12.5S exhibits a comparable ORR activity (half-wave potential of 0.901 V) to Pt/C (0.903 V) and a superior OER activity (overpotential of 272 mV at 10 mA cm-2) to RuO2 (299 mV). CoFe@NCNTs-12.5S also exhibits ultralow charge transfer resistances (ORR-6.36 Ω and OER-0.21 Ω) and an excellent potential difference of 0.617 V. The sulfidation-induced (CoFe)(S2)2/CoFe heterojunctions can accelerate interfacial charge transfer process. Tubular structure not only disperses the (CoFe)(S2)2/CoFe heterostructure, but also reduces the corrosion of active-sites to enhance catalysis stability. Zinc-air battery with CoFe@NCNTs-12.5S achieves a high specific capacity (718.1 mAh g-1), maintaining a voltage gap of 0.957 V after 400 h. This work reveals the potential of interface engineering for boosting ORR/OER activities of alloys via in-situ heterogenization.