Calcium Carbonate Formation in the Presence of Biopolymeric Additives
Published on: May 14, 2019
Reactive CaCO3 Formation from CO2 and Methanolic Ca(OH)2 Dispersions: Transient Methoxide Salts, Carbonate Esters and
Thokozile A Kathyola1,2, Elizabeth A Willneff1,3, Colin J Willis4
1School of Chemical and Process Engineering, University of Leeds, Leeds LS2 9JT, U.K.
Abstract:
A combination of ex situ and in situ characterization techniques was used to determine the mechanism of calcium carbonate (CaCO3) formation from calcium hydroxide (Ca(OH)2) dispersions in methanol/water (CH3OH/H2O) systems. Mid-infrared (mid-IR) analysis shows that in the absence of carbon dioxide (CO2) Ca(OH)2 establishes a reaction equilibrium with CH3OH, forming calcium hydroxide methoxide (Ca(OH)(OCH3)) and calcium methoxide (Ca(OCH3)2). Combined ex situ mid-IR, thermogravimetric analysis (TGA), X-ray diffraction (XRD), X-ray absorption spectroscopy and scanning electron microscopy examination of the reaction product formed in the presence of CO2 reveals the formation of calcium dimethylcarbonate (Ca(OCOOCH3)2). This strongly suggests that carbonation takes place by reaction with the Ca(OCH3)2 formed from a Ca(OH)2 and CH3OH reaction. Time-resolved XRD indicates that in the presence of H2O the Ca(OCOOCH3)2 ester releases CH3OH and CO2, forming ACC, which subsequently transforms into vaterite and then calcite. TGA reveals that thermal decomposition of Ca(OCOOCH3)2 in the absence of H2O mainly leads to the reformation of Ca(OCH3)2, but this is accompanied by a significant parallel reaction that releases dimethylether (CH3OCH3) and CO2. CaCO3 is the final product in both decomposition pathways. For CH3OH/H2O mixtures containing more than 50 mol % H2O, direct formation of calcite from Ca(OH)2 becomes the dominant pathway, although the formation of some Ca(OCOOCH3)2 was still evident in the in situ mid-IR spectra of 20 and 40 mol % CH3OH systems. In the presence of ≤20 mol % H2O, hydrolysis of the ester led to the formation of an ACC sol-gel. In both the 90 and 100 mol % CH3OH systems, diffusion-limited ACC → vaterite → calcite transformations were observed. Traces of aragonite were also detected. We believe that this is the first time that these reaction pathways during the carbonation of Ca(OH)2 in a methanolic phase have been systematically and experimentally characterized.
More Related Videos
11:14Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent
Published on: February 21, 2017
10:18Dynamic Pore-scale Reservoir-condition Imaging of Reaction in Carbonates Using Synchrotron Fast Tomography
Published on: February 21, 2017
Related Concept Videos
01:24Hydration of Cement
03:07Solubility Equilibria
The...
01:24Carbonation Shrinkage
The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
04:01Factors Affecting Solubility
01:26Alkali Aggregate Reaction in Concrete
01:02Loss of Carboxy Group as CO2: Decarboxylation of β-Ketoacids