Facile fabrication of degradable, serrated polyethylene diacrylate microneedles using stereolithography

Microneedles have the potential for minimally invasive drug delivery. However, they are constrained by absence of rapid, scalable fabrication methods to produce intricate arrays and serrations for enhanced adhesion. 3D printing techniques like stereolithography (SLA) are fast, scalable modalities but SLAs require non-degradable and stiff resins. This work attempts to overcome this limitation by utilizing a poly (ethylene glycol diacrylate) (PEGDA, F3) resin and demonstrating its compatibility with a commercial SLA printer. FESEM images showed high printing efficiency of customized bioinks (F3) similar to commercial resins using SLA 3D printer. Mechanical endurance tests of whole MNA showed that MNs array printed from F3 resin (485 ± 5.73 N) required considerably less force than commercial F1 resin (880 ± 32.4 N). Penetration performance of F1 and F3 was found to be 10.8 ± 2.06 N and 0.705 ± 0.03 N. In-vitro degradation study in PBS showed that MNs fabricated from F3 resin exhibited degradation after 7 days, which was not observed with the commercial F1 resin provided by the manufacturer. The histology of porcine skin exhibited formation of triangular pores with pore length of 548 μm and efficient penetration into the deeper dermal layer. In conclusion, PEGDA can be used as for fabricating degradable, serrated solid MNs over commercial resin.