Rapidly one-step fabrication of durable superhydrophobic graphene surface with high temperature resistance and...

High temperature resistant and self-cleaning superhydrophobic flexible film has potential application value in lunar exploration. In this paper, a novel method of magnetic field-assisted ultrafast laser induced plasma was proposed to fabricate strongly superhydrophobic graphene on polyimide film with multi-level micro-nano structure. The longitudinal magnetic field contributed to constrain the induced plasma in the lateral direction so as to form a plasma plume with high temperature and high energy density. The multi-level micro-nano graphene structures with better ordering and superhydrophobicity were fabricated, which had a contact angle of 163.1° and a roll-off angle of 1.5°, as well as hydrophobic CC bond content of 72.82 %. The droplets can achieve obvious bouncing at different heights of 1 cm and 5 cm on surfaces at different angles of 0°, 5° and 10°. The contact angle was still greater than 160° after 25 days of aging treatment and heating at 300 °C for 40 min. The water droplets before and after the heating of the sample can push the dust off the surface, showing excellent high temperature resistance and self-cleaning performance.