Optimization of TIG welding process parameters using Taguchi technique for the joining of dissimilar metals of AA5083...

This research paper aims to optimize the TIG welding parameters to join dissimilar metals of AA5083 and AA7075 using the Taguchi technique. The TIG welding current and root gap of butt geometry configuration are considered input parameters, and welding characteristics such as tensile strength, 0.2% of yield strength, hardness, and impact energy are output responses. The base metals are joined according to the Taguchi L-09 design of experiments. The welded samples were inspected using the X-ray radiography method for internal defects. Tensile properties, hardness number, and impact energy of different welding coupons were evaluated by conducting the uni-axial testing, a Brinell hardness test, and an Izod impact test, respectively. A better weld strength of 224 MPa was observed at 210 A welding current, and the root gap of 1.5 mm was maintained. Better hardness and impact energy values were observed when the root gap of 1.5 mm and welding current of 220 A were maintained. The root gap is the primary factor influencing tensile strength enhancement, which accounts for 44.78% of the effect, followed by 40.5% welding current. Root gap is the parameter that affects the tensile properties, hardness number, and impact toughness the most. The findings of this paper suggest the optimal parameters for welding AA5083 and AA7075 dissimilar base metals, which are suitable for complex structures requiring both durability and resistance to harsh environments.