Towards device stability of perovskite solar cells through low-cost alkyl-terminated SFX-based hole transporting...

Developing cost-effective, high-efficiency, and stable hole transporting materials (HTMs) is crucial for replacing traditional spiro-OMeTAD in perovskite solar cells (PSCs) and achieving sustainable solar energy solutions. This work presents two novel air-stable HTMs based on a spiro[fluorene-9,9'-xanthene] (SFX) core functionalized with N-methylcarbazole (XC2-M) and N-hexylcarbazole (XC2-H) rings. These HTMs were synthesized via a straightforward, three-step process with good overall yields (∼40%) and low production costs. To further reduce device cost, carbon back electrodes were employed. The resulting PSCs, with a structure of FTO/SnO₂/Cs_0.05FA_0.73MA_0.22Pb(I_0.77Br_0.23)₃/HTM/C achieved power conversion efficiencies (PCEs) of 13.5% (XC2-M) and 10.2% (XC2-H), comparable to the reference spiro-OMeTAD device (12.2%). The choice of alkyl chain on the HTM significantly impacts film morphology and device stability. The XC2-H device exhibited exceptional long-term stability, retaining approximately 90% of its initial PCE after 720 h of storage in 30-40% humidity air without encapsulation. This surpasses the performance of both the spiro-OMeTAD (55% retention) and XC2-M (68% retention) devices. The superior stability of XC2-H is attributed to its highly hydrophobic nature and the formation of a compact, smooth film due to interdigitation of the hexyl chains. The straightforward synthesis of XC2-H from commercially available materials offers a promising approach for large-scale PSC production.