Novel Eu³⁺-Doped Glasses in the MoO₃-WO₃-La₂O₃-B₂O₃ System: Preparation, Structure and Photoluminescent Properties

Novel multicomponent glasses with nominal compositions of (50-x)MoO₃:xWO₃:25La₂O₃:25B₂O₃, x = 0, 10, 20, 30, 40, 50 mol% doped with 3 mol % Eu₂O₃ were prepared using a conventional melt-quenching method. Their structure, thermal behavior and luminescent properties were investigated by Raman spectroscopy, differential thermal analysis and photoluminescence spectroscopy. The optical properties of the glasses were investigated by UV-vis absorption spectroscopy and a determination of the refractive index. Physical parameters such as density, molar volume, oxygen molar volume and oxygen packing density were determined. The glasses are characterized by a high glass transition temperature. Raman analysis revealed that the glass structure is built up mainly from tetrahedral (MoO₄)^2- and (WO₄)^2- units providing Raman bands of around 317 cm^-1, 341-352 cm^-1, 832-820 cm^-1 and 928-935 cm^-1. At the same time, with the replacement of MoO₃ with WO₃ some fraction of WO₆ octahedra are produced, the number of which increases with the increasing WO₃ content. A strong red emission from the ⁵D₀ level of Eu³⁺ ions was registered under near-UV (397 nm) excitation using the ⁷F₀ → ⁵L₆ transition of Eu³⁺. Photoluminescence (PL) emission gradually increases with increasing WO₃ content, evidencing that WO₃ is a more appropriate component than MoO₃. The integrated fluorescence intensity ratio R (⁵D₀ → ⁷F₂/⁵D₀ → ⁷F₁) was calculated to estimate the degree of asymmetry around the active ion, suggesting a location of Eu³⁺ in non-centrosymmetric sites. All findings suggest that the investigated glasses are potential candidates for red light-emitting phosphors.