Enhanced Synthesis of Poly(1,4-butanediol itaconate) via Box-Behnken Design Optimization

At present, there are too few organ and tissue donors. Due to the needs of the medical market, scientists are seeking new solutions. Those can be found in tissue engineering by synthesizing synthetic cell scaffolds. We have decided to synthesize a potential UV-crosslinked bio-ink for 3D printing, poly(1,4-butanediol itaconate), in response to emerging needs. Diol polyesters are commonly investigated for their use in tissue engineering. However, itaconic acid makes it possible to post-modify the obtained polymer via UV-crosslinking. This work aims to optimize the synthesis of poly(1,4-butanediol itaconate) in the presence of a catalyst, zinc acetate, without using any toxic reactant. The experiments used itaconic acid and 1,4-butanediol using the Box-Behnken mathematical planning method. The input variables were the amount of the catalyst used, as well as the time and temperature of the synthesis. The optimized output variables were the percentage conversion of carboxyl groups, the percentage of unreacted C=C bonds, and the product's visual and viscosity analysis. The significance of the varying synthesis parameters was determined in each statistical model. The optimum conditions were as follows: amount of catalyst 0.3%_nCOOH, reaction time 4 h, and temperature 150 °C. The temperature had the most significant impact on the product characteristics, mainly due to side reactions. Experimentally developed models of the polymerization process enable the effective synthesis of a polymer "tailor-made" for a specific application.