Synthesis of Amphiphilic Polyacrylates as Peelable Coatings for Optical Surface Cleaning

Optical instruments require extremely high precision, and even minor surface contamination can severely impact their performance. Peelable coatings offer an effective and non-damaging method for removing contaminants from optical surfaces. In this study, an amphiphilic polyacrylate copolymer (PMLEA) was synthesized via solution radical copolymerization using the lipophilic monomer lauryl acrylate (LA) and hydrophilic monomers ER-10, methyl methacrylate (MMA), and butyl acrylate (BA). The structure and molecular weight of the copolymer were characterized using Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance (NMR), and gel permeation chromatography (GPC). The hydrophilic-lipophilic balance, surface tension, and wettability of the copolymer were analyzed through water titration, the platinum plate method, and liquid contact angle tests. The cleaning performance of the copolymer coating on quartz glass surface contaminants was evaluated using optical microscopy and Ultraviolet-Visible Near-Infrared (UV-Vis-NIR) spectroscopy. The study examined the effect of varying the ratio of LA to ER-10 on the hydrophilicity, lipophilicity, cleaning efficiency, and mechanical properties of the copolymer coating. The results showed that when the mass ratio of LA to ER-10 was 1:2, the synthesized copolymer exhibited optimal performance in removing dust, grease, and fingerprints from quartz glass surfaces. The coating had a tensile strength of 2.57 MPa, an elongation at break of 183%, and a peeling force of 2.07 N m^-1.