Study on Dynamic Recrystallization under Thermal Cycles in the Process of Direct Energy Deposition for 316 L...

In the process of directed energy deposition (DED), the grain structure of the deposited samples is determined by two aspects. The first is the initial solidification grain structure; the second is the effect of the upper thermal cycle on the solidified grain structure of the lower layer. Dynamic recrystallization and grain growth can be activated under suitable strain and the temperature resulting from thermal cycles. The evolution of grain size and the geometric dislocation density (GND) of austenitic stainless steel 316 L under different strains and temperatures caused by thermal cycles was investigated. It is found that dynamic recrystallization requires an appropriate level of accumulated strain, temperature, and initial grain size. Under <2% accumulated strain and 400-1200 °C conditions caused by 30 layers of thermal cycles, fully dynamic recrystallization occurs with coarse initial grains (CIG), leading to the complete coarsening of grains. However, relatively fine initial grains (FIG) under the same conditions only display partial dynamic recrystallization. The next 2-4% strain and 400-700 °C by 60 layers of thermal cycles make up the driving force of fully dynamic recrystallization, and the grains coarsen completely. Larger accumulated strain (4-6%) and lower temperature (400-600 °C) by 90 layers of thermal cycles and FIG provide more nucleation sites for dynamic recrystallization, which leads to little coarsening of grains even after fully dynamic recrystallization. Temperature, accumulated strain, and the amount of δ-ferrite promote the formation of sub-grains during dynamic recrystallization caused by thermal cycles, which leads to the increase in GND.