Hydrogen Embrittlement Behavior of API X70 Linepipe Steel under Ex Situ and In Situ Hydrogen Charging

This study investigates the hydrogen embrittlement behavior of API X70 linepipe steel. The microstructure was primarily composed of a dislocation-rich bainitic microstructure and polygonal ferrite. Slow strain-rate tests (SSRTs) were performed under both ex situ and in situ electrochemical hydrogen charging conditions to examine the difference between hydrogen diffusion and trapping behaviors. The ex situ SSRTs showed almost the same tensile properties as air and a limited brittle fracture confined to near the surface. In contrast, the in situ SSRTs showed an abrupt failure after the maximum tensile load, leading to a brittle fracture across the entire fracture surface with stress-oriented hydrogen-induced cracking (SOHIC). The crack trace analysis results indicated that SOHIC propagation paths were influenced by localized hydrogen accumulation due to high-stress fields. As a result, the dominant hydrogen embrittlement mechanisms, such as hydrogen-enhanced localized plasticity (HELP) and hydrogen-enhanced decohesion (HEDE), changed. These findings provide critical insights into the microstructural factors affecting hydrogen embrittlement, which are essential for the design of hydrogen-resistant steels in hydrogen infrastructure applications.