Microstructure Evolution of the Interface in SiC_f/TiC-Ti₃SiC₂ Composite under Sequential Xe-He-H Ion Irradiation and...

A new type of SiC_f/TiC-Ti₃SiC₂ composite was prepared by the Spark Plasma Sintering (SPS) method in this work. The phase transformation and interface cracking of this composite under ion irradiation (single Xe, Xe + He, and Xe + He + H ions) and subsequent annealing were analyzed using transmission electron microscopy (TEM), mainly focusing on the interface regions. Xe ion irradiation resulted in the formation of high-density stacking faults in the TiC coatings and the complete amorphization of SiC fibers. The implanted H ions exacerbated interface coarsening. After annealing at 900 °C for 2 h, the interface in the Xe + He + H ion-irradiated samples was seriously damaged, resulting in the formation of large bubbles and cracks. This damage occurred because the H atoms reduced the surface free energy, thereby promoting the nucleation and growth of bubbles. Due to the absorption effect of the SiC_f/TiC interface on defects, the SiC fiber areas near the interface recovered back to the initial nano-polycrystalline structure after annealing.