Manganese Oxide-Doped Hierarchical Porous Carbon Derived from Tea Leaf Waste for High-Performance Supercapacitors

Hierarchical porous carbon derived from discarded biomass for energy storage materials has attracted increasing research attention due to its cost-effectiveness, ease of fabrication, environmental protection, and sustainability. Brewed tea leaves are rich in heteroatoms that are beneficial to capacitive energy storage behavior. Therefore, we synthesized high electrochemical performance carbon-based composites from Tie guan yin tea leaf waste using a facile procedure comprising hydrothermal, chemical activation, and calcination processes. In particular, potassium permanganate (KMnO₄) was incorporated into the potassium hydroxide (KOH) activation agent; therefore, during the activation process, KOH continued to erode the biomass precursor, producing abundant pores, and KMnO₄ synchronously underwent a redox reaction to form MnO nanoparticles and anchor on the porous carbon through chemical bonding. MnO nanoparticles provided additional pseudocapacitive charge storage capabilities through redox reactions. The results show that the amount of MnO produced is proportional to the amount of KMnO₄ incorporated. However, the specific surface area of the composite material decreases with the incorporated amount of KMnO₄ due to the accumulation and aggregation of MnO nanoparticles, thereby even blocking some micropores. Optimization of MnO nanocrystal loading can promote the crystallinity and graphitization degree of carbonaceous materials. The specimen prepared with a weight ratio of KMnO₄ to hydrochar of 0.02 exhibited a high capacitance of 337 F/g, an increase of 70%, owing to the synergistic effect between the Tie guan yin tea leaf-derived activated carbon and MnO nanoparticles. With this facile preparation method and the resulting high electrochemical performance, the development of manganese oxide/carbon composites derived from tea leaf biomass is expected to become a promising candidate as an energy storage material for supercapacitors.