The Dissolution Behavior of Pyrite and Chalcopyrite During Low-Temperature Pressure Oxidation: Chalcopyrite Influence...

The research of this paper was carried out on the low-temperature (100 ± 2 °C) pressure (0.2-0.8 MPa) leaching of pyrite, chalcopyrite and their mixture. According to experiments on chalcopyrite dissolution, increasing the oxygen pressure from 0.2 up to 0.8 MPa had a slight effect on chalcopyrite dissolution. Oxygen pressure and initial sulfuric acid concentration in the range of 10-50 g/L had the greatest positive effect on the pyrite oxidation. The SEM and EDX mappings indicate the chalcopyrite and pyrite surfaces to be passivated by elemental sulfur. The oxidation degree of pyrite in its mixture with chalcopyrite increased significantly from 54.5 up to 80.3% in 0-240 min. The reaction time is relative to the dissolution of the individual mineral, while the dissolution of chalcopyrite remained virtually unchanged. The addition of Cu (II) and Fe (III) ions does not influence pyrite dissolution when chalcopyrite is added in a leaching process, which can be explained by the formation of an electrochemical link between the minerals. The positive effect of chalcopyrite addition is associated with a decreased formation of elemental sulfur on the surface of pyrite. The described method can be used for the hydrometallurgical processing of copper raw materials with increased pyrite content, as well as for the pretreatment of copper concentrates with gold-rich pyrite concentrates to increase the recovery of gold and silver.