Feasibility of Exceeding 20% Efficiency for Kesterite/c-Silicon Tandem Solar Cells Using an Alternative Buffer Layer:...

Tandem solar cells have the potential to be more efficient than the Shockley-Queisser limit imposed on single junction cells. In this study, optical and electrical modeling based on experimental data were used to investigate the possibility of boosting the performance of kesterite/c-Si tandem solar cells by inserting an alternative nontoxic TiO₂ buffer layer into the kesterite top subcell. First, with SCAPS-1D simulation, we determined the data reported for the best kesterite (CZTS (Eg = 1.5 eV)) device in the experiments to be used as a simulation baseline. After obtaining metric parameters close to those reported, the influence on the optoelectronic characteristics of replacing CdS with a TiO₂ buffer layer was studied and analyzed. Different top subcell absorbers (CZTS0.8Se0.2 (Eg = 1.4 eV), CZTS (Eg = 1.5 eV), CZTS (Eg = 1.6 eV), and CZT0.6Ge0.4S (Eg = 1.7 eV)) with different thicknesses were investigated under AM1.5 illumination. Then, to achieve current matching conditions, the c-Si bottom subcell, with an efficiency at the level of commercially available subcells (19%), was simulated using various top subcells transmitting light calculated using the transfer matrix method (TMM) for optical modeling. Adding TiO₂ significantly enhanced the electrical and optical performance of the kesterite top subcell due to the decrease in parasitic light absorption and heterojunction interface recombination. The best tandem device with a TiO₂ buffer layer for the top subcell with an optimum bandgap equal to 1.7 eV (CZT0.6Ge0.4S4) and a thickness of 0.8 µm achieved an efficiency of approximately 20%. These findings revealed that using a TiO₂ buffer layer is a promising way to improve the performance of kesterite/Si tandem solar cells in the future. However, important optical and electrical breakthroughs are needed to make kesterite materials viable for tandem applications.