Novel antimicrobial biodegradable composite films as packaging materials based on shellac/chitosan, and ZnAl₂O₄ or...

ZnAl₂O₄ and CuAl₂O₄ spinel nanoparticles were prepared by a modified Pechini method and used with the natural chitosan (CS) and shellac (SH) polymers to form novel composite membranes as promising food packaging materials. The selection of ZnAl₂O₄ and CuAl₂O₄ spinel nanoparticles was based on their antibacterial characteristics, availability, and economy. Using a straightforward and adaptable solution mixing and casting method, the bio-composites were created. The mechanical, physical, antibacterial, homogeneity and air permeability properties of composite films were investigated. The film structure was evaluated in terms of component interactions using FTIR spectra. The addition of 10% SH increased the tensile strength, percentage strain at maximum load, Young's modulus, and burst strength by 114-101%, 3.6-8.4, 103-119, and 179-153% for low and middle M.wt./CS respectively. Chitosan/shellac-CuAl₂O₄ composite has superior properties compared to ZnAl₂O₄ composite. In general, 0.05% spinel provides a composite having better qualities than that of 0.1 additions. Middle M.wt. chitosan provides a composite with superior properties compared to that of low M.wt. The incorporation of ZnAl₂O₄ or CuAl₂O₄ enhanced the thermal stability of the SH/CS composite. ZnAl₂O₄ provides superior thermal stability than CuAl₂O₄. When shellac/CS film structure is treated with the previously indicated ZnAl₂O₄ or CuAl₂O₄ formulation, the % swelling decreases along with an increasing in the gel fraction. The antimicrobial assessment using inhibition zone diameter and shake flask methods showed that a composite of 1:9 shellac/chitosan/0.05% of CuAl₂O₄ exerted the highest Gram-positive antibacterial activity against B. mycoides (21 mm), and C. albicans (22 mm). So, these enhancements make chitosan/shellac/ZnAl₂O₄ or CuAl₂O₄ composite films a good alternative to producing food packaging materials.