Water Sorption on Isoreticular CPO-27-Type MOFs: From Discrete Sorption Sites to Water-Bridge-Mediated Pore...

Pore engineering is commonly used to alter the properties of metal-organic frameworks. This is achieved by incorporating different linker molecules (L) into the structure, generating isoreticular frameworks. CPO-27, also named MOF-74, is a prototypical material for this approach, offering the potential to modify the size of its one-dimensional pore channels and the hydrophobicity of pore walls using various linker ligands during synthesis. Thermal activation of these materials yields accessible open metal sites (i.e., under-coordinated metal centers) at the pore walls, thus acting as strong primary binding sites for guest molecules, including water. We study the effect of the pore size and linker hydrophobicity within a series of Ni²⁺-based isoreticular frameworks (i.e., Ni₂L, L = dhtp, dhip, dondc, bpp, bpm, tpp), analyzing their water sorption behavior and the water interactions in the confined pore space. For this purpose, we apply water vapor sorption analysis and Fourier transform infrared spectroscopy. In addition, defect degrees of all compounds are determined by thermogravimetric analysis and solution ¹H nuclear magnetic resonance spectroscopy. We find that larger defect degrees affect the preferential sorption sites in Ni₂dhtp, while no such indication is found for the other materials in our study. Instead, strong evidence is found for the formation of water bridges/chains between coordinating water molecules, as previously observed for hydrophobic porous carbons and mesoporous silica. This suggests similar sorption energies for additional water molecules in materials with larger pore sizes after saturation of the primary binding sites, resulting in more bulk-like water arrangements. Consequently, the sorption mechanism is driven by classical pore condensation through H-bonding anchor sites instead of sorption at discrete sites.