High-Performance Ammonia QCM Sensor Based on SnO₂ Quantum Dots/Ti₃C₂T_x MXene Composites at Room Temperature

Ammonia (NH₃) gas is prevalent in industrial production as a health hazardous gas. Consequently, it is essential to develop a straightforward, reliable, and stable NH₃ sensor capable of operating at room temperature. This paper presents an innovative approach to modifying SnO₂ colloidal quantum dots (CQDs) on the surface of Ti₃C₂T_x MXene to form a heterojunction, which introduces a significant number of adsorption sites and enhances the response of the sensor. Zero-dimensional (0D) SnO₂ quantum dots and two-dimensional (2D) Ti₃C₂T_x MXene were prepared by solvothermal and in situ etching methods, respectively. The impact of the mass ratio between two materials on the performance was assessed. The sensor based on 12 wt% Ti₃C₂T_x MXene/SnO₂ composites demonstrates excellent performance in terms of sensitivity and response/recovery speed. Upon exposure to 50 ppm NH₃, the frequency shift in the sensor is -1140 Hz, which is 5.6 times larger than that of pure Ti₃C₂T_x MXene and 2.8 times higher than that of SnO₂ CQDs. The response/recovery time of the sensor for 10 ppm NH₃ was 36/54 s, respectively. The sensor exhibited a theoretical detection limit of 73 ppb and good repeatability. Furthermore, a stable sensing performance can be maintained after 30 days. The enhanced sensor performance can be attributed to the abundant active sites provided by the accumulation/depletion layer in the Ti₃C₂T_x/SnO₂ heterojunction, which facilitates the adsorption of oxygen molecules. This work promotes the gas sensing application of MXenes and provides a way to improve gas sensing performance.