Green Synthesis of Ag and Cu Nanoparticles Using E. telmateia Ehrh Extract: Coating, Characterization, and...

PEEK-based implant materials have gained increasing attention as an alternative to titanium due to their biocompatibility and bone-like elasticity. However, PEEK's surface quality and wear resistance are lower than those of metals. This study aimed to enhance the bioactivity and surface quality of PEEK by coating it with silver and copper nanoparticles synthesized via a green method using Equisetum telmateia Ehrh. extract. PEEK samples (Ø 25 mm, 3 mm thick) were coated with single and double layers using spray (airbrush-spray) and drop-coating methods. Comprehensive analyses including SEM, EDX, FT-IR, UV-Vis, surface roughness, release studies, antioxidant and cytotoxicity activity, and antibacterial tests were conducted on the coated samples. The results demonstrated that AgNPs and CuNPs coatings significantly improved the surface quality of PEEK. SEM analysis revealed particle sizes ranging from 48 to 160 nm for AgNPs and 50-135 nm for CuNPs, with superior dispersion obtained using the airbrush-spray method. Surface roughness measurements showed a reduction of 17-33% for AgNPs-coated samples and 7-15% for CuNPs-coated samples compared to uncoated PEEK, with airbrush-spray coatings providing smoother surfaces. Antioxidant activity tests indicated that AgNPs provided 35% higher antioxidant activity compared to CuNPs. Additionally, antibacterial tests revealed that AgNPs exhibited a higher zone of inhibition (up to 14 mm for S. aureus and 18 mm for E. coli) compared to CuNPs, which exhibited zones of 8 mm and 10 mm, respectively. This study concludes that green-synthesized AgNPs, in particular, enhance the bioactivity and surface properties of PEEK, making it a promising material for biomedical applications such as infection-resistant implants.