The Effect of Aging Process Conditions on the Thermal Properties of Poly(Dimethylsiloxane)-Based Silicone Rubber

Silicone rubbers based on poly(dimethylsiloxane) (PDMS) are crosslinked elastomers commonly used in various branches of industry, especially as packing materials in elements for high-temperature service. In addition to high temperatures, mechanical loading may influence their structure during their work, and, as a consequence, their thermal properties may change. This study's findings on the degradation mechanism under aging conditions are not just necessary, but also crucial for their satisfactory application. The aim of the study was a detailed and comprehensive evaluation of the aging processes of commercial ELASTOSIL^® LR 3842/50 A/B, considering structural changes based on thermal analysis accompanied by mass spectroscopy, X-ray analysis, and infrared spectroscopy. The aging process was carried out at 125 °C and 175 °C, without and with 11 kg of loading. The obtained results showed that the aging of PDMS increased their thermal stability. It was the most visible for PDMS aging at 175 °C under load. It was attributed to secondary crosslinking and the post-curing process. Observed changes in polymer structure did not indicate its degradation. This is a significant finding, especially considering that a temperature of 175 °C is close to the critical temperature given by the producer (180 °C), above which the use of stabilizing agents is recommended.