Analysis of Mechanical Properties and Printing Orientation Influence of Composite Resin for 3D Printing Compared to...

This study aimed to compare the flexural strength, surface roughness, and microhardness of a resin for three-dimensional (3D) printing and a conventional composite resin and to evaluate whether the printing orientation influences these properties. To evaluate the flexural resistance, test specimens were produced and divided into four groups: three groups of resins for 3D printing with inclinations of 0°, 45°, and 90° and one group of conventional composite resin. Forty discs were produced and subjected to a sandpaper-polishing sequence, and the surface roughness was measured using a roughness meter. The Vickers microhardness (HV) test was performed at three different points, and the average was obtained. The results were subjected to ANOVA statistical analysis and Tukey's test. There were statistical differences in the flexural strength and microhardness between the conventional resin and the resin used for 3D printing. No statistical difference in surface roughness was observed. The resin for 3D printing exhibited lower flexural strength and microhardness than conventional composite resins. We concluded that the resin for 3D printing had lower flexural strength and HV than the conventional composite resin but similar surface roughness. The printing orientation did not affect the flexural strength, whereas the hardness increased as the printing angle increased.