Preparation and Properties of Fe-Based Double Perovskite Oxide as Cathode Material for Intermediate-Temperature Solid...

Double perovskite oxides with mixed ionic and electronic conductors (MIECs) have been widely investigated as cathode materials for solid oxide fuel cells (SOFCs). Classical Fe-based double perovskites, due to their inherent low electronic and oxygen ionic conductivity, usually exhibit poor electrocatalytic activity. The existence of various valence states of B-site ions modifies the material's catalytic activity, indicating the possibility of the partial substitution of Fe by higher-valence ions. LaBaFe_2-xMo_xO_5+δ (x = 0, 0.03, 0.05, 0.07, 0.1, LBFM_x) is used as intermediate-temperature solid oxide fuel cell (IT-SOFC) cathode materials. At a doping concentration above 0.1, the Mo substitution enhanced the cell volume, and the lattice expansion caused the formation of the impurity phase, BaMoO₄. Compared with the parent material, Mo doping can regulate the oxygen vacancy concentration and accelerate the oxygen reduction reaction process to improve the electrochemical performance, as well as having a suitable coefficient of thermal expansion and excellent electrode stability. LaBaFe_1.9Mo_0.1O_5+δ is a promising cathode material for IT-SOFC, which shows an excellent electrochemical performance, with this being demonstrated by having the lowest polarization resistance value of 0.017 Ω·cm² at 800 °C, and the peak power density (PPD) of anode-supported single-cell LBFM_0.1|CGO|NiO+CGO reaching 599 mW·cm^-2.