Enhanced Dielectric Properties and Antibacterial Activity of Natural Rubber by Modification with Poly(Acrylic...

This work aims to enhance natural rubber's dielectric properties and antibacterial activity by incorporating silver nanoparticles and titanium dioxide. Deproteinized natural rubber (DPNR) was modified through the graft copolymerization of acrylic acid and acrylamide using N', N'-Methylenebisacrylamide as a crosslinking agent, resulting in poly(acrylic acid-co-acrylamide)-modified, deproteinized natural rubber (MDPNR). This modification facilitated coordination with silver ions and interaction with titanium dioxide. Silver nanoparticles were generated under heat and pressure. Modified natural rubber composites containing silver nanoparticles and titanium dioxide (MDPNR/Ag-TiO₂) were prepared. Scanning electron microscopy (SEM) revealed well-distributed silver in the modified natural rubber matrix, while agglomeration of titanium dioxide was observed at a high loading. Both MDPNR and MDPNR/Ag-TiO₂ showed high thermal stability compared to DPNR. The MDPNR/Ag-TiO₂ composites exhibited higher Tg and lower tan δ, indicating higher stiffness due to the restriction of chain movement compared to that in MDPNR. DPNR exhibited a low dielectric constant, enhanced by poly(acrylic acid-co-acrylamide) modification and silver nanoparticle/titanium dioxide incorporation. Incorporating 0.5 phr of AgNO₃ and 2.5 phr of TiO₂ in the composites increased the dielectric constant by 1.33 times compared to that of MDPNR. MDPNR showed no antibacterial activity, while the MDPNR/Ag-TiO₂ composites exhibited promising antibacterial activity against Staphylococcus aureus and Escherichia coli.