Insights into the photoaging behavior of biodegradable and nondegradable microplastics: Spectroscopic and molecular...

Biodegradable plastics are increasingly used as a potential alternative to nondegradable plastics to tackle plastic pollution. However, recent studies have raised concerns about the ecological risks posed by biodegradable microplastics (MPs), which mainly focused on the risks generated by MPs themselves, neglecting the risks associated with the MPs derived dissolved organic matter (DOM). Therefore, this study selected polylactic acid (PLA) MPs with 50 µm particle size and polystyrene (PS) MPs with 50 µm and 500 nm particle sizes as representatives of biodegradable and nondegradable MPs, respectively, to comparative investigate their photoaging behavior, particularly the differences in DOM release. The results showed that both PLA-MPs and PS-MPs exhibited considerable photoaging under ultraviolet irradiation, accompanied by different color changes (PS turned yellow and PLA turned grayish brown), which were attributed to the different functional groups produced on their surfaces after photoaging (PS-MPs: CO, PLA-MPs: terminal -COOH). Additionally, excitation-emission matrix characterization combined with parallel factor analysis revealed that 50 µm PLA-MPs (16-23 %) released more protein-like low molecular weight DOM during photoaging than that of both 50 µm PS-MPs (7-13 %) and 500 nm PS-MPs (8-18 %). Fourier transform-ion cyclotron resonance-mass spectrometry (FT-ICR-MS) further confirmed that PLA-MPs (41.4 %) produced more unstable DOM easily utilized by microorganisms than that of 50 µm PS-MPs (6.3 %) and 500 nm PS-MPs (7.9 %). These results together suggested that biodegradable MPs with small particle size derived DOM may have a greater impact on microbial activity and carbon cycle than that of nondegradable MPs.