Two-step sintering suppresses grain growth and improves flexural strength of dental zirconia

This study aimed to elucidate the effect of various two-step sintering (TSS) protocols on the physical, mechanical, and optical properties of partially stabilized zirconia with different yttria dopant concentrations (Y-PSZ).

Disc-shaped specimens were obtained from most widely used commercial dental zirconia powders of various Y contents (Tosoh Corp.) by uniaxial pressing followed by cold-isostatic pressing. Densification was carried out using TSS protocols with varying temperatures for both sintering steps. Relative density (ρ_Rel), microstructure, and phase content were analyzed. Biaxial flexural strength (σ) and translucency parameter (TP) were evaluated.

The TSS results were compared with optimized conventional sintering (CS) results from a previous study for the same Y-PSZ compositions. TSS 3Y-PSZ and 4Y-PSZ reached similar ρ_Rel to those of their CS counterparts, whereas 5Y-PSZ failed to achieve that regardless of TSS protocol. TSS yielded less cubic phase compared to CS, especially for 3Y-PSZ and for higher temperatures. TSS suppressed the grain growth throughout the temperature range investigated, promoting smaller grains than CS (p < 0.05). The TP values for TSS Y-PSZ were lower than those of CS (p ≤ 0.0001), except for 3Y-PSZ. The σ values for TSS Y-PSZ were significantly higher than those of CS (p ≤ 0.0002).

TSS increased strength without significantly jeopardizing the optical properties of various Y-PSZ compositions relative to their CS counterparts. This alternative sintering method appears to be a promising technique for controlling grain growth while eliminating porosities in dental Y-PSZ ceramics, thus potentially enhancing the clinical longevity of zirconia restorations.