Graphene nanosheets decorated with heterostructured ruthenium sulfide as catalyst for enhanced hydrogen evolution
Warisha Naseeb1,2, Muhammad Kaleem Khosa1, Awal Noor3
1Department of Chemistry, Government College University, Faisalabad, Pakistan.
Abstract:
In present findings, a simple pyrolysis technique was applied to decorate S and N doped graphene with RuS2-CoO nanoparticles synthesizing a heterostructured nanocomposite RuS2-CoO@SNG. XPS results demonstrate the elemental composition of these nanomaterials with the hint of metal-metal charge transfer phenomenon likely due to heterostructure composition. These modifications led to a significant active surface area resulting in elevated electrocatalytic performance. In comparison to benchmark Pt/C at -60 mV in 1 M KOH, hydrogen evolution reaction (HER) reached at current density around 10 mA cm-2 at -90 mV overpotential. The stability test displayed excellent results with a decrease of 2 mV in overpotential at current density of 10 mA cm-2. Results indicate that such heterostructured nanocomposites can be used as an effective catalyst for HER.
Related Concept Videos
02:50Catalysis
02:17Reduction of Alkenes: Asymmetric Catalytic Hydrogenation
The metal catalyst used can be either heterogeneous or homogeneous. When hydrogenation of an alkene generates a chiral center, a pair of enantiomeric products is expected to form. However, an enantiomeric excess of one of the products can be facilitated using an enantioselective reaction or an...