Investigation of Gamma Ray Shielding Characteristics of Binary Composites Containing Polyester Resin and Lead Oxide

Ionizing radiation plays an essential role across various fields but also poses significant health risks, requiring effective shielding solutions. This study focuses on the photon shielding properties of PbO-reinforced composites, specifically PbO-0, PbO-2, PbO-4, PbO-6, PbO-8, and PbO-10, through experimental measurements of photon energies ranging from 59.5 keV to 1408.0 keV. The measurements were taken using an HPGe detector. Experimental results were compared to theoretical calculations. Among the tested composites, PbO-10, which contains the highest concentration of lead oxide (PbO), provided the most effective radiation shielding. This sample demonstrated superior mass and linear attenuation coefficients, offering excellent protection at low photon energies. Furthermore, PbO-10 exhibited the lowest half-value layer (HVL) and tenth-value layer (TVL) values, indicating its efficiency in reducing radiation intensity with thinner material layers. It was determined that the experimental TVL results for PbO-O, PbO-2, PbO-4, PbO-6, PbO-8, and PbO-10 at 59.5 keV photon energy were 9.95, 5.98, 4.77, 3.67, 3.22, and 2.71 cm, respectively. With these outstanding attenuation capabilities, PbO-10 is deemed highly suitable for use in medical, industrial, and radiation-heavy environments. In summary, this research emphasizes the effectiveness of PbO-reinforced composites in gamma-ray shielding, with PbO-10 emerging as the top performer, demonstrating great potential for applications that require durable and efficient radiation protection.