Acid-Hydrolysis-Assisted Cellulose Nanocrystal Isolation from Acacia mearnsii de Wild. Wood Kraft Pulp

Cellulose nanocrystals (CNC) receive great attention for their physical and optical properties, high surface area, high tensile strength, rigidity (Young's modulus up to 140 GPa), and ease of surface modification. However, controlling the properties of CNC is still challenging, given the wide variety of pulp sources and the complexity of finding suitable processing conditions. In the present study, acid hydrolysis efficiently isolated CNC from wood Acacia mearnsii brown kraft pulp (AMKP). Initially, the AMKP was delignified by the treatment with acidified sodium chlorite. The Acacia mearnsii kraft pulp obtained was then subjected to acid hydrolysis with sulfuric acid at concentrations of 50 to 58% 45 °C for 60 min. The hydrolysate was sonicated in an ultrasonic processor for 30 min. The chemical composition was determined by Fourier transform infrared spectroscopy (FTIR), crystallinity by X-ray diffraction (XRD), zeta potential by Zetasizer ZS equipment, thermal stability by thermogravimetric analysis (TGA), and morphology by transmission electron microscopy (TEM) to verify the effect of acid concentration on the yield and properties of CNC. The optimization of the isolation process demonstrated that the maximum yield of 41.95% can be obtained when AMWP was hydrolyzed with sulfuric acid at a concentration of 54%. It was possible to isolate CNC with a crystallinity index between 71.66% and 81.76%, with the onset of thermal degradation at 240 °C; zeta potential of -47.87 to 57.23 mV; and rod-like morphology, with lengths and widths between 181.70 nm and 260.24 nm and 10.36 nm and 11.06 nm, respectively. Sulfuric acid concentration significantly affected the yield of acid hydrolysis, allowing the isolation of CNC with variable dimensions, high thermal stability, high crystallinity index, and great colloidal stability in aqueous medium.