A Rod-like Bi₂O₃ Photocatalyst Derived from Bi-Based MOFs for the Efficient Adsorption and Catalytic Reduction of...

Heavy metal ion pollution poses a serious threat to the natural environment and human health. Photoreduction through Bi-based photocatalysts is regarded as an advanced green technology for solving environmental problems. However, their photocatalytic activity is limited by the rapid recombination of photogenerated e^- and h⁺ pairs and a low photo-quantum efficiency. In this work, an optimal precursor of Bi-based MOFs was identified by using different solvents, and rod-like Bi₂O₃ materials were derived by in situ oxidation of Bi atoms in the precursor. The adsorption and photocatalytic reduction efficiency of the prepared Bi₂O₃ materials for Cr(VI) were evaluated under visible light irradiation. The results showed that the prepared materials had a large specific surface area and enhanced visible light absorption. Bi₂O₃(DMF/MeOH-3)-400 had a large specific surface area and many active adsorption sites, and it had the highest adsorption of Cr(VI) (49.13%) among the materials. Bi₂O₃(DMF/MeOH-3)-400 also had the highest photocatalytic reduction efficiency, and it achieved 100% removal of 10 mg·L^-1 Cr(VI) within 90 min under light. In addition, the material showed remarkable stability after three consecutive photocatalytic cycles. The enhanced photocatalytic performance was mainly attributed to the fast separation of electron-hole pairs and efficient electron transfer in the MOF-derived materials, which was confirmed by electrochemical tests and PL spectroscopy. Reactive species trapping experiments confirmed that electrons were the main active substances; accordingly, a possible photocatalytic mechanism was proposed. In conclusion, this work provides a new perspective for designing novel photocatalysts that can facilitate the removal of Cr(VI) from water.