Effect of Al₇Cu₂Fe Particles on the Anisotropic Mechanical Properties and Formability of Al-Zn-Mg-Cu-Based Alloy...

The presence of Al₇Cu₂Fe particles, formed due to Fe impurities in Al-Zn-Mg-Cu alloys, significantly impacts mechanical properties and formability, which is crucial for the use of these alloys in the automotive and aerospace industries. In this study, we prepared Al-Zn-Mg-Cu-based alloy sheets with large (LF), small (SF), and no (NF) Al₇Cu₂Fe particles to explore their effects on recrystallization and mechanical behavior. These sheets were fabricated using controlled cooling rates and subsequent thermo-mechanical processing. Fine dispersion of Al₇Cu₂Fe particles in the SF sheet led to a substantial reduction in grain size (16.5 μm) and an increase in yield strength (168.6 MPa), albeit with lower ductility (24.6%). In contrast, the NF sheet exhibited a lower yield strength (141.5 MPa) but superior ductility (35.8%) due to the absence of Al₇Cu₂Fe particles, which prevented premature fracture. The SF sheet demonstrated lower anisotropy in ductility due to the uniform recrystallized grain orientations, while the LF and NF sheets exhibited significant anisotropy in yield strength. These findings indicate that optimizing Al₇Cu₂Fe particle dispersion is key to balancing the strength, ductility, and anisotropy in Al-Zn-Mg-Cu alloys.