New Polymer-Carbon Lustrous Carbon Precursor in Synthetic Molding Sands-Part I: Studies on the Properties of Sands

Beata Grabowska1, Artur Bobrowski1, Dariusz Drożyński1

  • 1Faculty of Foundry Engineering, AGH University of Krakow (AGH University), Reymonta 23, 30-059 Krakow, Poland.

Materials (Basel, Switzerland)
|January 8, 2025
PubMed

Keywords:
bentonitecastfoundrylustrous carbonmontmorillonitepolyethyleneshungite

More Related Videos

Surface Properties of Synthesized Nanoporous Carbon and Silica Matrices09:31

Surface Properties of Synthesized Nanoporous Carbon and Silica Matrices

Published on: March 27, 2019

9.4K
Author Spotlight: Standardizing the Development of Amine-Based Silica Composites as CO2 Adsorbents for Direct Air Capture08:00

Author Spotlight: Standardizing the Development of Amine-Based Silica Composites as CO2 Adsorbents for Direct Air Capture

Published on: September 29, 2023

2.2K

Related Concept Videos

Network Covalent Solids02:18

Network Covalent Solids

Network covalent solids contain a three-dimensional network of covalently bonded atoms as found in the crystal structures of nonmetals like diamond, graphite, silicon, and some covalent compounds, such as silicon dioxide (sand) and silicon carbide (carborundum, the abrasive on sandpaper). Many minerals have networks of covalent bonds.
To break or to melt a covalent network solid, covalent bonds must be broken. Because covalent bonds are relatively strong, covalent network solids are typically...
12.9K
Fineness of Cement01:15

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
787
Deleterious Substances in Aggregate01:25

Deleterious Substances in Aggregate

Deleterious substances in aggregates can be detrimental to the quality and durability of concrete. These substances include organic impurities like loam, which interfere with cement hydration and are usually present in the sand. These prevent a good bond between aggregate and cement paste. Organic impurities can be detected using the colorimetric test, where the darkness of a solution after agitation indicates the level of organic content.
Another type of impurity is clay and fine material that...
867
Superplasticizers01:30

Superplasticizers

Superplasticizers are advanced admixtures that enhance the workability of concrete by lowering the water content without compromising the strength of the material. These substances are highly effective water reducers, improving concrete flow, making it easier to work with, and enabling concrete to reach inaccessible areas or densely reinforced sections without mechanical vibration. The key components in superplasticizers are either sulfonated melamine or naphthalene formaldehyde condensates,...
468
Carbonation Shrinkage01:24

Carbonation Shrinkage

Atmospheric CO2 penetrates the concrete's pores and, in the presence of moisture, forms carbonic acid, which then reacts with calcium hydroxide in the hydrated cement, forming calcium carbonate. This process reduces the concrete's volume and is termed carbonation shrinkage.
The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
662
Design Example: Aggregate Gradation01:24

Design Example: Aggregate Gradation

The right type and quality of aggregates are crucial for concrete as they significantly influence its properties, mix proportions, and cost-effectiveness. If different sources are available for sand, the commonly used fine aggregate in concrete, the selection of sand is primarily based on its gradation.
The grading, or particle-size distribution, of sand is determined using sieve analysis, with standard sizes ranging from 150 μm to 10 mm (ASTM No. 100 sieve to 3⁄8 in. sieve). Sand is...
470