The Effect of Post Heat Treatment on the Microstructure and Mechanical Properties of Cold-Sprayed Zn-6Cu Deposits

To explore the feasibility of preparing Zn alloy bulk, Zn-6Cu deposit was prepared by cold-spraying additive manufacturing. Microstructure, tensile and wear behavior were investigated before and after heat treatment. Cold-sprayed Zn-6Cu deposit was constituted by irregular flattening particles and pores after heat treatment. Zn-6Cu deposits were composed of Zn and CuZn₅ phases in addition to ZnO phase regardless of heat treatment, but the full width at half maximum of both the CuZn₅ and the Zn phase were varied. The yield strength and ultimate tensile strength of Zn-6Cu deposits after post heat treatment were, respectively, increased from 83.8 ± 28.7 MPa and 159.6 ± 44.5 MPa to 89.4 ± 24.4 MPa and 223.8 ± 37.1 MPa. Fracture morphology after tensile testing exhibited main features of dimples, pores and cleaving particles. The friction coefficient and wear rate of Zn-6Cu deposits were increased after heat treatment, and the corrosive wear exhibited a lower friction coefficient and wear rate than the dry wear due to the lubricant of simulated body fluid. Grooves and localized delamination were the main wear features of Zn-6Cu deposits regardless of both the heat treatment and wear condition. This result indicates a potential application of cold-sprayed Zn-6Cu deposits comparable to the casting ones.