Crack Sealing in Concrete with Biogrout: Sustainable Approach to Enhancing Mechanical Strength and Water Resistance

Concrete, as the most widely used construction material globally, is prone to cracking under the influence of external factors such as mechanical loads, temperature fluctuations, chemical corrosion, and freeze-thaw cycles. Traditional concrete crack repair methods, such as epoxy resins and polymer mortars, often suffer from a limited permeability, poor compatibility with substrates, and insufficient long-term durability. Microbial biogrouting technology, leveraging microbial-induced calcium carbonate precipitation (MICP), has emerged as a promising alternative for crack sealing. This study aimed to explore the potential of Bacillus pasteurii for repairing concrete cracks to enhance compressive strength and permeability performance post-repair. Experiments were conducted to evaluate the bacterial growth cycle and urease activity under varying concentrations of Ca²⁺. The results indicated that the optimal time for crack repair occurred 24-36 h after bacterial cultivation. Additionally, the study revealed an inhibitory effect of high calcium ion concentrations on urease activity, with the optimal concentration identified as 1 mol/L. Compressive strength and water absorption tests were performed on repaired concrete specimens. The compressive strength of specimens with cracks of varying dimensions improved by 4.01-11.4% post-repair, with the highest improvement observed for specimens with 1 mm wide and 10 mm deep cracks, reaching an increase of 11.4%. In the water absorption tests conducted over 24 h, the average mass water absorption rate decreased by 31.36% for specimens with 0.5 mm cracks, 29.06% for 1 mm cracks, 27.9% for 2 mm cracks, and 28.2% for 3 mm cracks. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses confirmed the formation of dense calcium carbonate precipitates, with the SEM-EDS results identifying calcite and vaterite as the predominant self-healing products. This study underscores the potential of MICP-based microbial biogrouting as a sustainable and effective solution for enhancing the mechanical and durability properties of repaired concrete.