Fracture resistance and mode of failure of modified Polyether-ether-ketone versus lithium disilicate endocrowns

Mohamed G A Kharboush1, Hesham I Othman2, Mohamed F Aldamaty3,4

  • 1Department of Fixed Prosthodontics, Faculty of Dental Medicine, Al-Azhar University, Cairo, 11651, Egypt. mohamed_gamal@azhar.edu.eg.

BMC Oral Health
|January 8, 2025
PubMed
Abstract

Keywords:
EndocrownFailure modeFracture resistanceLithium disilicatePolyether-ether-ketone

More Related Videos

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

13.4K
An Improved Mechanical Testing Method to Assess Bone-implant Anchorage11:51

An Improved Mechanical Testing Method to Assess Bone-implant Anchorage

Published on: February 10, 2014

15.4K

Related Concept Videos

Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
2.1K
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
143
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
172
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
100
Fiber Reinforced Concrete01:22

Fiber Reinforced Concrete

Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...
68