A Co-Blended and Compounded Photosensitive Resin with Improved Mechanical Properties and Thermal Stability for Nail...

UV-curable bio-based resins are widely used in the UV curing field. However, the current UV-curable bio-based resins for the application of nail polish still have the problems of too high viscosity and insufficiently excellent mechanical properties. In this study, a soybean oil-based acrylate photosensitive resin is synthesized by using epoxidized soybean oil as a raw material and reacting it with acrylic acid. The results show that the viscosity of soybean oil-based acrylate can achieve 8.31 Pa∙s, and the UV-cured film prepared by soybean oil-based acrylate and anhydride derivatives can obtain a tensile strength of 35.36 MPa and an elongation at break of 67.8%. In addition, the soybean oil-based acrylate is further reacted with isophorone diisocyanate to obtain soybean oil-based polyurethane acrylate, which can be thermally stable at 90 °C for 7 d. And then, the UV-cured film constructed by soybean oil-based polyurethane acrylate and anhydride derivatives are prepared, and the elongation at the break of the cured films can be up to 320%. This work provides a solvent-free approach by using biomass raw materials to form polyurethane acrylic resins, which have promising potential in the application of nail polish.