Enhanced Tribological and Mechanical Properties of Copper-Modified Basalt-Reinforced Epoxy Composites

The increasing demand for high-performance materials in industrial applications highlights the need for composites with enhanced mechanical and tribological properties. Basalt fiber-reinforced polymers (BFRP) are promising materials due to their superior strength-to-weight ratio and environmental benefits, yet their wear resistance and tensile performance often require further optimization. This study examines how adding copper (Cu) powder to epoxy resin influences the mechanical and tribological properties of BFRP composites. Epoxy matrices, modified with 5%, 10%, and 15% weight fractions (wf.%) of copper powder, were reinforced with BFRP-type fabric, using a vacuum bag manufacturing method. Mechanical tests, including bending and tensile tests, showed notable improvements in tensile strength and flexural modulus due to copper addition, with higher copper (Cu) content enhancing ductility. Tribological tests using a pin-on-disk tribometer revealed reduced wear rates and an optimized coefficient of friction. Statistical analysis and 3D microscopy identified wear mechanisms such as delamination and protective copper film formation. The results highlight the significant potential of copper-modified BFRP composites for applications demanding superior mechanical and tribological performance.