Synthesis and characterization of photo-cross-linkable quince seed-based hydrogels for soft tissue engineering...

The convenience, versatility, and biocompatibility of photocrosslinkable hydrogel precursors make them promising candidates for developing tissue engineering scaffolds. However, the current library of photosensitive materials is limited. This study reports, for the first time, the modification of quince seed mucilage (QS) with glycidyl methacrylate (GM), resulting in the synthesis of methacrylated QS (QSGM). The chemical composition and structure of QS were analyzed. The effects of reaction time, temperature, QS concentration, and GM/QS ratio on the degree of methacrylation, as well as the physicochemical, rheological, mechanical, and biological properties of the synthesized materials were explored. Chemical characterization using ¹H NMR and FTIR confirmed the successful methacrylation of QS. Hydrogels fabricated from QSGMs at a 0.5 wt% concentration exhibited high swelling ratios of 320 to 580 g/g, and compressive strengths between 0.6 ± 0.1 and 1.2 ± 0.3 kPa. No significant changes in the rheological properties of hydrogel precursors were observed. Moreover, QSGM-based hydrogels supported cell encapsulation for 14 days with minimal cytotoxicity and immune cell activation. Finally, as a proof of concept, the potential use of QSGM for 3D printing was demonstrated. Overall, the results highlight the significant potential of QSGMs as a biomaterial of choice for soft tissue engineering applications.