Composite Sorbents Based on Polymeric Se-Derivative of Amidoximes and SiO₂ for the Uranium Removal from Liquid...

A new composite material with enhanced sorption-selective properties for uranium recovery from liquid media has been obtained. Sorbents were synthesized through a polycondensation reaction of a mixture of 4-amino-N'-hydroxy-1,2,5-oxadiazole-3-carboximidamide (hereinafter referred to as amidoxime) and SiO₂ in an environment of organic solvents (acetic acid, dioxane) and highly porous SiO₂. To establish optimal conditions for forming the polymer sorption-active part and the synthesis as a whole, a series of composite adsorbents were synthesized with varying amidoxime/matrix ratios (35/65, 50/50, 65/35). The samples were characterized with FT-IR, XRD, SEM, EDX, XRFES spectroscopy and TGA. Under static conditions of uranium sorption, the dependence of the efficiency of radionuclide recovery from mineralized solutions of various acidities on the ratio of the initial components was established. In the pH range from 4 to 8 (inclusive), the uranium removal efficiency exceeds 95%, while the values of the distribution coefficients (Kd) exceed 10⁴ cm³g^-1. It was demonstrated that an increase in the surface development of the sorbents enhances such kinetic parameters of uranium sorption as diffusion rate by 10-20 times compared to non-porous materials. The values of the maximum static capacity exceed 700 mg g^-1. The enhanced availability of adsorption centers, achieved through the use of a porous SiO₂ matrix, significantly improves the kinetic parameters of the adsorbents. A composite with optimal physicochemical and sorption properties (amidoxime/matrix ratio of 50/50) was examined under dynamic conditions of uranium sorption. It was found that the maximum dynamic sorption capacity of porous materials is four times greater compared to that of a non-porous adsorbent Se-init. The effective filter cycle exceeds 3200 column volumes-twice that of an adsorbent with a monolithic surface. These results indicate the promising potential of the developed materials for uranium sorption from liquid mineralized media under dynamic conditions across a wide pH range.