Non-Stoichiometric Ba_xMn_0.7Cu_0.3O₃ Perovskites as Catalysts for CO Oxidation: Optimizing the Ba Content

In this work, a series of Ba_xMn_0.7Cu_0.3O₃ samples (x: 1, 0.9, 0.8, and 0.7, BxMC) was synthesized, characterized, and used as catalysts for CO oxidation reaction. All formulations were active for CO oxidation in the tested conditions. A correlation between the electrical conductivity, obtained by impedance spectroscopy, and the reducibility of the samples, obtained by H₂-TPR, was observed. The Ba_0.8Mn_0.7Cu_0.3O₃ composition (B0.8MC) showed the best catalytic performance (comparable to that of the 1% Pt/Al₂O₃ reference sample) during tests conducted under conditions similar to those found in the exhaust gases of current gasoline engines. The characterization data suggest the simultaneous presence of a high Mn(IV)/Mn(III) surface ratio, oxygen vacancies, and reduced copper species, these two latter being key properties for ensuring a high CO conversion percentage as both are active sites for CO oxidation. The reaction temperature and the reactant atmosphere composition seem to be the most important factors for achieving a good catalytic performance, as they strongly determine the location and stability of the reduced copper species.