High-Performance Hydrogen Sensing at Room Temperature via Nb-Doped Titanium Oxide Thin Films Fabricated by Micro-Arc...

Metal oxide semiconductor (MOS) hydrogen sensors offer advantages, such as high sensitivity and fast response, but their challenges remain in achieving low-cost fabrication and stable operation at room temperature. This study investigates Nb-doped TiO₂ (NTO) thin films prepared via a one-step micro-arc oxidation (MAO) with the addition of Nb₂O₅ nanoparticles into the electrolyte for room-temperature hydrogen sensing. The characterization results revealed that the incorporation of Nb₂O₅ altered the film's morphology and phase composition, increasing the Nb content and forming a homogeneous composite thin film. Hydrogen sensing tests demonstrated that the NTO samples exhibited significantly improved sensitivity, selectivity, and stability compared to undoped TiO₂. Among the fabricated samples, NTO thin film prepared at Nb₂O₅ concentration of 6 g/L (NTO-6) showed the best performance, with a broad detection range, excellent sensitivity, rapid response, and good specificity to hydrogen. A strong linear relationship between response values and hydrogen concentration (10-1000 ppm) highlights its potential for precise hydrogen detection. The enhanced hydrogen sensing mechanism of NTO thin films primarily stems from the influence of Nb₂O₅; nanoparticles doping in the anatase-phase TiO₂ structure on the semiconductor surface depletion layer, as well as the improved charge transfer and additional adsorption sites provided by the Nb/Ti composite metal oxides, such as TiNb₂O₇ and Ti_0.95Nb_0.95O₄. This study demonstrates the potential of MAO-fabricated Nb-doped TiO₂ thin films as efficient and reliable hydrogen sensors operating at room temperature, offering a pathway for novel gas-sensing technologies to support clean energy applications.