Analysis of the Effect of Human Type I Collagen-Derived Peptide on Bone Regenerative Capacity and Comparison with...

Background and Objectives: Autologous bone grafting is the first choice for reconstructive surgery in bone defects due to trauma or malignant tumors. However, there is an increasing demand for minimally invasive alternatives involving bone regeneration using artificial materials. Biomimetic materials that replicate the body's microscopic structure, such as Cellnest^®, are gaining attention. Cellnest is a xeno-free recombinant peptide based on human type I collagen, containing a rich Arg-Gly-Asp (RGD) motif related to cell adhesion. The aim of this study was to compare the effects of Cellnest with existing collagen materials (Pelnac^®, Integra^®, Terudermis^®) on bone regeneration and elucidate the underlying mechanisms. Materials and Methods: In vivo experiments involved a rat model of calvarial bone defects, in which Cellnest and other collagen materials were implanted into the defect area. Bone formation was assessed after 4 weeks using micro-computed tomography (micro-CT) and histological analysis. In vitro experiments included the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT), adhesion, and migration assays, and a real-time polymerase chain reaction using rapidly expanding cells (RECs) to explore the mechanisms of Cellnest's bone regenerative capacity. Results: The micro-CT analysis showed that the regenerated bone area was significantly greater in the Cellnest group (72.3%) than in the Pelnac^® (25.5%), Integra^® (31.6%), and Terudermis^® (38.3%) groups. The histological analysis confirmed similar trends, with Cellnest showing 42.2% bone regeneration, outperforming the other materials. The in vitro assays revealed that Cellnest promoted cell proliferation, adhesion, and migration. Gene expression analysis demonstrated that Cellnest significantly increased the levels of the bone formation markers ALP and COL1. Conclusions: Cellnest, a human type I collagen-like peptide rich in RGD motifs, enhances bone regeneration by promoting MSC adhesion and migration, and bone formation-related gene expression. The findings suggest its potential as an effective material for bone defect reconstruction.